ASTM A105 Kompożizzjoni kimika u materjali ekwivalenti
1. ASTM A105 Kompożizzjoni Kimika (Piż%)
| Element | Ħtieġa standard | Valur tipiku |
|---|---|---|
| Karbonju (Ċ) | Inqas minn jew daqs 0. 35% | 0.27-0.33% |
| Manganiż (MN) | 0.60-1.05% | 0.70-0.90% |
| Fosfru (P) | Inqas minn jew daqs 0. 035% | 0.020-0.030% |
| Kubrit (i) | Inqas minn jew daqs 0. 040% | 0.015-0.025% |
| Silikon (SI) | 0.10-0.35% | 0.15-0.30% |
| Ram (CU) | Inqas minn jew daqs 0. 40% | 0.10-0.25% |
| Nickel (Ni) | Inqas minn jew daqs 0. 40% | Inqas minn jew daqs 0. 20% |
| Kromju (CR) | Inqas minn jew daqs 0. 30% | Inqas minn jew daqs 0. 15% |
| Molibdenu (MO) | Inqas minn jew daqs 0. 12% | Inqas minn jew daqs 0. 05% |
| Vanadium (V) | Inqas minn jew daqs 0. 08% | Inqas minn jew daqs 0. 03% |
Noti:
BaxxP/SIl-kontenut itejjeb il-weldabilità.
IkkontrollatC \/ mnIl-proporzjon jibbilanċja s-saħħa u d-duttilità.
2. ASTM A105 Materjali ekwivalenti
Skont l-istandard u r-reġjun
| Reġjun \/ standard | Gradi ekwivalenti | Differenzi ewlenin |
|---|---|---|
| Ewropa (EN) | 1.0460 (C22.8) | C \/ mn simili, iżda en jippermetti p \/ s ogħla |
| Ġappun (JIS) | SF440A | Kompożizzjoni kważi identika |
| Iċ-Ċina (GB) | 20mn (锻件用) | Kemmxejn ogħla mn (0. 70-1. 00%) |
| L-Indja (IS) | Huwa 2062 gr. A | Firxa usa 'ta' kompożizzjoni |
Ekwivalenti funzjonali
| Materjal | Uża każ | Paragun |
|---|---|---|
| ASTM A350 LF2 | Servizz ta 'temperatura baxxa (<-29°C) | Impatt aħjar ebusija |
| ASTM A694 F42 \/ F52 | Pajpijiet bi pressjoni għolja | Qawwa ta 'rendiment ogħla |
| ASTM A182 F304 | Ambjenti korrużivi | Alternattiva tal-istainless steel |
3. Tqabbil tal-proprjetajiet ewlenin
| Proprjetà | ASTM A105 | A350 LF2 | En 1.0460 |
|---|---|---|---|
| Qawwa tat-tensjoni | Akbar minn jew daqs 485 MPa | Akbar minn jew daqs 485 MPa | 410-560 MPA |
| Saħħa tar-rendiment | Akbar minn jew daqs 250 MPa | Akbar minn jew daqs 250 MPa | Akbar minn jew daqs 245 MPa |
| Test tal-impatt | Mhux meħtieġ | -46 Grad Charpy Meħtieġ | Temp tal-kamra biss |
| Forom komuni | Flanġijiet, fittings | Flanġijiet, valvi | Forgings, bars |
4. Linji Gwida għall-Għażla tal-Materjal
Għal pajpijiet ġenerali (ilma, żejt, gass): ASTM A105 (kosteffikaċi)
Għal temperaturi sub-żero: ASTM A350 LF2 (ebusija aħjar)
Għas-Servizz Sour (H2S): ASTM A105N (Normalizzat) + NACE MR0175 Konformità
Għal proġetti tal-UE: En 10222-2 p265GH (l-eqreb ekwivalenti konformi mal-ped)
5. FAQs
M: L-ASTM A105 jista 'jintuża għal applikazzjonijiet ta' temperatura baxxa?
A: Biss għal-29 grad- Taħt dan, użaA350 LF2(iċċertifikat għal -46 grad).
M: L-istainless steel ASTM A105?
A: Le, huwaazzar tal-karbonju- Għal reżistenza għall-korrużjoni, ikkunsidraA182 F304/F316.
M: Xi tfisser "N" f'A105N?
A: Trattament tas-sħana normalizzatgħal struttura mtejba tal-qamħ u proprjetajiet ta 'impatt.
M: Ekwivalenti għal AISI 1020?
A: Kompożizzjoni simili, iżda A105 hijafalsifikat(Mhux irrumblat \/ mitfugħ bħal 1020).
Għandek bżonn għajnuna biex tagħżel materjali?Ipprovdi l-kundizzjonijiet tas-servizz tiegħek (pressjoni, temperatura, midja) għal rakkomandazzjonijiet imfassla apposta.